DIN 50969-3:2017-08
Prevention of hydrogen-induced brittle fracture of high-strength steel building elements - Part 3: Post operational influences and extended testing / Note: Date of issue 2017-07-07
| Fecha edición: |
2018-06-01
Anulada
|
|---|---|
| Fecha cancelación: | 2018-06-01 |
| Idiomas disponibles: | Alemán |
| Resumen: | This standard specifies procedures for the assessment of the risk of hydrogen pollution and for the detection of a brittle fracture risk during the corrosion loading of components with coatings and in hot-dip galvanizing on high-tensile steel components. |
| Keywords: | Blank forms|Bracing test|Brittle fractures|Brittleness|Chemical plating|Coatings|Components|Corrosion|Cracking|Electrochemical coating|Fracture|Heat treatment|High-tensile steels|Hydrogen|Hydrogen embrittlement|Materials testing|Metal coatings|Resistance|Steels|Surface treatment|Temperature|Test duration|Testing |
| ICS: | 77.140.01 - Productos de fundición y productos de acero en general |
| CTN: | |
|
Reemplazo Normas |
Es reemplazada por DIN 50969-3:2018-06 |