ASTM B985 - 24
Standard Practice for Sampling Aluminum Ingots, Billets, Castings and Finished or Semi-Finished Wrought Aluminum Products for Compositional Analysis
| Fecha edición: |
2024-07-01
En Vigor
|
|---|---|
| Idiomas disponibles: | Inglés |
| Resumen: | |
| Keywords: | |
| Scope: | 1.1 This practice describes procedures for sampling unwrought aluminum ingots, billets, castings and finished or semi-finished wrought aluminum products to obtain a representative sample for determining chemical composition. 1.1.1 Chemical compositions determined from samples obtained in accordance with this standard practice may differ from the bulk chemical composition determined from samples taken when ingots or castings are poured. These differences can be due to elemental segregation that occurs during solidification, procedures that remove enriched material (for example, ingot scalping), or procedures that remove depleted areas (for example, removal of the riser from a casting). 1.1.2 Analysis of samples obtained from unwrought aluminum ingots, billets, and castings and finished or semi-finished wrought aluminum products can be used to determine if the piece sampled meets The Aluminum Association, Inc. registered chemical composition limits or other specified chemical composition limits for the alloy. Analysis of such samples shall not supersede the analysis of samples taken during pouring of castings or ingots in accordance with Practices E716 and analyzed in accordance with Test Methods E1251, E3061, or EN 14242 and shall not be used for determining compliance with chemical composition requirements for an entire cast lot or part thereof. Note 1: Pieces may include ingots, forgings, coils, sheets, extrusions, castings, and so forth. A single unwrought ingot or billet may produce multiple finished or semi-finished pieces. Note 2: Certification of entire cast lots should be determined using samples taken during pouring of castings or ingots in accordance with Practices E716 and analyzed in accordance with Test Methods E1251, E3061, or EN 14242. 1.2 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
| ICS: | 77.150.10 - Productos de aluminio |
| CTN: | B07.05 - B07.05 |
|
Otras Relaciones |
Es referenciada por E1251 - 24 Es referenciada por B0491_B0491M-23 Es referenciada por B0373-19 Es referenciada por B0210_B0210M-19A Es referenciada por B0179-18 Es referenciada por B0221M-21 Es referenciada por B0026_B0026M-18E01 Es referenciada por E0716-16R21E02 Es referenciada por B0316_B0316M-20 Es referenciada por B0234-17 Es referenciada por B0221-21 Es referenciada por B0429_B0429M-20 Es referenciada por B0308_B0308M-20 Es referenciada por B0618_B0618M-18E01 Es referenciada por B0108_B0108M-19 Es referenciada por B0969_B0969M-18E01 Es referenciada por B0632_B0632M-24 Es referenciada por B0955_B0955M-18 Es referenciada por B0085_B0085M-18E01 Es referenciada por B0209_B0209M-21A |