ASTM E112 - 25
Standard Test Methods for Determining Average Grain Size
| Aviso: | Las normas ASTM en lectura se visualizan a través del área decliente. Los archivos no se pueden descargar | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Fecha edición: |
2025-06-15
En Vigor
|
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Idiomas disponibles: | Inglés | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Resumen: | |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Keywords: | ALA grain size; anisotropy index; area fraction; ASTM grain size number; calibration; equiaxed grains; etchant; grain boundary; grains; grain size; intercept count; intercept length; intersection count; non-equiaxed grains; twin boundaries ; | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Scope: | 1.1 These test methods cover the measurement of average grain size and include the comparison procedure, the planimetric (or Jeffries) procedure, and the intercept procedures. These test methods may also be applied to nonmetallic materials with structures having appearances similar to those of the metallic structures shown in the comparison charts. These test methods apply chiefly to single phase grain structures but they can be applied to determine the average size of a particular type of grain structure in a multiphase or multiconstituent specimen. 1.2 These test methods are used to determine the average grain size of specimens with a unimodal distribution of grain areas, diameters, or intercept lengths. These distributions are approximately log normal. These test methods do not cover methods to characterize the nature of the following distributions. Characterization of grain size in specimens with duplex grain size distributions is described in Test Methods E1181. Measurement of individual, very coarse grains in a fine grained matrix is described in Test Methods E930. 1.3 These test methods deal only with determination of planar grain size, that is, characterization of the two-dimensional grain sections revealed by the sectioning plane. Determination of spatial grain size, that is, measurement of the size of the three-dimensional grains in the specimen volume, is beyond the scope of these test methods. 1.4 These test methods describe techniques performed manually using either a standard series of graded chart images for the comparison method or simple templates for the manual counting methods. Utilization of semi-automatic digitizing tablets or automatic image analyzers to measure grain size is described in Test Methods E1382. 1.5 These test methods deal only with the recommended test methods and nothing in them should be construed as defining or establishing limits of acceptability or fitness of purpose of the materials tested. 1.6 The measured values are stated in SI units, which are regarded as standard. Equivalent inch-pound values, when listed, are in parentheses and may be approximate. 1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. 1.8 The paragraphs appear in the following order:
1.9 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| ICS: | 77.040.01 - Ensayos de metales en general | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| CTN: | E04.08 - E04.08 | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
Otras Relaciones |
Es referenciada por F1537 - 20 Es referenciada por A240/A240M - 25a Es referenciada por F138 - 19 Es referenciada por A941 - 25b Es referenciada por F2393 - 12(2025) Es referenciada por A131/A131M - 19 Es referenciada por B43 - 20 Es referenciada por F2063 - 18 Es referenciada por B251/B251M - 17 Es referenciada por F1058 - 25 Es referenciada por A914/A914M - 19(2024) Es referenciada por G108 - 23 Es referenciada por B708 - 25 Es referenciada por F2257 - 22 Es referenciada por A988/A988M - 23 Es referenciada por A1014/A1014M - 16(2021) Es referenciada por E531 - 24 Es referenciada por A891/A891M - 24 Es referenciada por B444 - 23 Es referenciada por A193/A193M - 25 |
Normas citadas
Libros relacionados
Normas relacionadas
Colecciones temáticas relacionadas